| Quantity: | |
|---|---|
M6
GOSHEN
Stainless Steel SEMS Hex Cap Machine Screw
| Product Name | Stainless Steel SEMS Hex Cap Machine Screw |
| Material | Stainless Steel |
| Grade | A2,A4 |
| Finish | Plain, Passivated, Dacromet Black, Dacromet Gray, Nickel Plated, Color Zinc Plated, Black Oxide, Hot-Dipped Galvanizing, etc. |
| Head Type | Binding Head, Hex Head, Pan Head, Hex Washer Head, Socket Head, Truss Head, Flat Head, Oval Head, Round Head, Pan Washer Head, etc. |
| Drive Type | Phillips, Slotted, Phillips-Slotted Combo, Pozi, Socket, Torx, Torx-Slotted Combo, Torx Pin, etc. |
| Size | Metric, Inch |
| Customized | Available |
| Sample | Free in stock (The express should be paid by buyer) |
Material
| SS316 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | P≤ | S≤ | Si≤ | Ni | Cr | Mo |
| 0.08 | 2.00 | 0.045 | 0.030 | 1 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | |
| 316 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
| 304 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 | |
| 304 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
Stainless Steel SEMS Hex Cap Machine Screw
| Product Name | Stainless Steel SEMS Hex Cap Machine Screw |
| Material | Stainless Steel |
| Grade | A2,A4 |
| Finish | Plain, Passivated, Dacromet Black, Dacromet Gray, Nickel Plated, Color Zinc Plated, Black Oxide, Hot-Dipped Galvanizing, etc. |
| Head Type | Binding Head, Hex Head, Pan Head, Hex Washer Head, Socket Head, Truss Head, Flat Head, Oval Head, Round Head, Pan Washer Head, etc. |
| Drive Type | Phillips, Slotted, Phillips-Slotted Combo, Pozi, Socket, Torx, Torx-Slotted Combo, Torx Pin, etc. |
| Size | Metric, Inch |
| Customized | Available |
| Sample | Free in stock (The express should be paid by buyer) |
Material
| SS316 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | P≤ | S≤ | Si≤ | Ni | Cr | Mo |
| 0.08 | 2.00 | 0.045 | 0.030 | 1 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | |
| 316 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
| 304 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 | |
| 304 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |