Phillips Head Self Tapping Sheet Metal Screws
| Product Name | Stainless Steel 304 Phillips Head Self Tapping Sheet Metal Screws |
| Material | stainless steel |
| Color | Bright polisjed |
| Standard | DIN GB ISO JIS BA ANSI |
| Grade | SUS201, SUS304, SUS316, SUS410, SUS420 |
| Brade | Lyhc |
| OEM/ODM | Available |
| Used | building, industry ,machinery ect. |
| Delivery time | 3-15 days after received your payment |
Material
| SS316 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | P≤ | S≤ | Si≤ | Ni | Cr | Mo |
| 0.08 | 2.00 | 0.045 | 0.030 | 1 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | |
| 316 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
| 304 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 | |
| 304 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
Phillips Head Self Tapping Sheet Metal Screws
| Product Name | Stainless Steel 304 Phillips Head Self Tapping Sheet Metal Screws |
| Material | stainless steel |
| Color | Bright polisjed |
| Standard | DIN GB ISO JIS BA ANSI |
| Grade | SUS201, SUS304, SUS316, SUS410, SUS420 |
| Brade | Lyhc |
| OEM/ODM | Available |
| Used | building, industry ,machinery ect. |
| Delivery time | 3-15 days after received your payment |
Material
| SS316 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | P≤ | S≤ | Si≤ | Ni | Cr | Mo |
| 0.08 | 2.00 | 0.045 | 0.030 | 1 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | |
| 316 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
| 304 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 | |
| 304 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |