Stainless Steel DIN436 Square Washer
Product Description
Stainless Steel DIN436 Square Washer
Product Name | |
Material | Stainless Steel 304/316/316L |
OEM/Custom | YES |
Feature | 1.Corrosion resistant 2.Excellent life cycle 3.Environmentally friendly 4.High-Performance Fastening |
Standard Available | GB, DIN, ISO, ANSI, ASME, IFI, JIS, BSW, AS, Q, HJ, BS, PEN |
Material Available | Stainless Steel Titanium and Titanium Alloy Aluminum |
Packing | Box+Carton +Pallet or as per client's requirement |
Specification
| Suitable thread | M10 | M12 | M16 | M20 | M22 | M24 | M27 | M30 | M33 | M36 | M39 | M42 | M45 | M48 | M52 | ||
| d | Min= Nominal | 11 | 13.5 | 17.5 | 22 | 24 | 26 | 30 | 33 | 36 | 39 | 42 | 45 | 48 | 52 | 56 | |
| Max | 11.43 | 13.93 | 18.2 | 22.84 | 24.84 | 26.84 | 30.84 | 34 | 37 | 40 | 43 | 46 | 49 | 53.2 | 57.2 | ||
| s | Max= Nominal | 30 | 40 | 50 | 60 | 70 | 80 | 90 | 95 | 100 | 110 | 125 | 135 | 140 | 150 | 160 | |
| Min | 28.7 | 38.4 | 48.4 | 58.1 | 68.1 | 78.1 | 87.8 | 92.8 | 97.8 | 107.8 | 122.5 | 132.5 | 137.5 | 147.5 | 157.5 | ||
| h | Nominal | 3 | 4 | 5 | 5 | 6 | 6 | 6 | 6 | 6 | 8 | 8 | 8 | 8 | 10 | 10 | |
| Max | 3.6 | 4.6 | 6 | 6 | 7 | 7 | 7 | 7 | 7 | 9.2 | 9.2 | 9.2 | 9.2 | 11.2 | 11.2 | ||
| Min | 2.4 | 3.4 | 4 | 4 | 5 | 5 | 5 | 5 | 5 | 6.8 | 6.8 | 6.8 | 6.8 | 8.8 | 8.8 | ||
| Thousand pieces of weight (steel)≈kg | 20 | 45.7 | 88.7 | 126 | 209 | 275 | 348 | 385 | 423 | 685 | 895 | 1050 | 1120 | 1600 | 1820 | ||
Material
| 304 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 | |
| 304 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
| 316 Chemical Composition(%) | ||||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | Cu | MO | N |
| 0.017 | 0.98 | 0.25 | 0.0016 | 0.0414 | 16.23 | 10.08 | 0.32 | 2.06 | 0.037 | |
| 316 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |