DIN128 Stainless Steel Wave Spring Lock Washers
Product Description
Stainless Steel Wave Spring Lock Washers
Product Name | DIN128 Stainless Steel Wave Spring Lock Washers |
Material | Stainless Steel 304/316/316L |
OEM/Custom | YES |
Feature | 1.Corrosion resistant 2.Excellent life cycle 3.Environmentally friendly 4.High-Performance Fastening |
Standard Available | GB, DIN, ISO, ANSI, ASME, IFI, JIS, BSW, AS, Q, HJ, BS, PEN |
Material Available | Stainless Steel Titanium and Titanium Alloy Aluminum |
Packing | Box+Carton +Pallet or as per client's requirement |
Specification
| Nominal diameter | 2 | 2.5 | 3 | 3.5 | 4 | 5 | 6 | 7 | 8 | 10 | ||
| d | Min | 2.1 | 2.6 | 3.1 | 3.6 | 4.1 | 5.1 | 6.1 | 7.1 | 8.1 | 10.2 | |
| Max | 2.4 | 2.9 | 3.4 | 3.9 | 4.4 | 5.4 | 6.5 | 7.5 | 8.5 | 10.7 | ||
| dc | Max | 4.4 | 5.1 | 6.2 | 6.7 | 7.6 | 9.2 | 11.8 | 12.8 | 14.8 | 18.1 | |
| b | Nominal | 0.9 | 1 | 1.3 | 1.3 | 1.5 | 1.8 | 2.5 | 2.5 | 3 | 3.5 | |
| Max | 1 | 1.1 | 1.4 | 1.4 | 1.6 | 1.9 | 2.65 | 2.65 | 3.15 | 3.7 | ||
| Min | 0.8 | 0.9 | 1.2 | 1.2 | 1.4 | 1.7 | 2.35 | 2.35 | 2.85 | 3.3 | ||
| s | Nominal | 0.5 | 0.6 | 0.7 | 0.7 | 0.8 | 1 | 1.3 | 1.3 | 1.6 | 1.8 | |
| Max | 0.6 | 0.7 | 0.8 | 0.8 | 0.9 | 1.1 | 1.4 | 1.4 | 1.7 | 1.9 | ||
| Min | 0.4 | 0.5 | 0.6 | 0.6 | 0.7 | 0.9 | 1.2 | 1.2 | 1.5 | 1.7 | ||
| h | Min | 0.7 | 0.9 | 1.1 | 1.1 | 1.2 | 1.5 | 2 | 2 | 2.45 | 2.85 | |
| Max | 0.9 | 1.1 | 1.3 | 1.3 | 1.4 | 1.7 | 2.2 | 2.2 | 2.75 | 3.15 | ||
| Thousand pieces of weight (steel)≈kg | 0.035 | 0.055 | 0.09 | 0.1 | 0.15 | 0.3 | 0.7 | 0.75 | 1.3 | 2.1 | ||
| Nominal diameter | 12 | 14 | 16 | 18 | 20 | 22 | 24 | 27 | 30 | 36 | ||
| d | Min | 12.2 | 14.2 | 16.2 | 18.2 | 20.2 | 22.5 | 24.5 | 27.5 | 30.5 | 36.5 | |
| Max | 12.7 | 14.7 | 17 | 19 | 21.2 | 23.5 | 25.5 | 28.5 | 31.7 | 37.7 | ||
| dc | Max | 21.1 | 24.1 | 27.4 | 29.4 | 33.6 | 35.9 | 40 | 43 | 48.2 | 58.2 | |
| b | Nominal | 4 | 4.5 | 5 | 5 | 6 | 6 | 7 | 7 | 8 | 10 | |
| Max | 4.2 | 4.7 | 5.2 | 5.2 | 6.2 | 6.2 | 7.25 | 7.25 | 8.25 | 10.25 | ||
| Min | 3.8 | 4.3 | 4.8 | 4.8 | 5.8 | 5.8 | 6.75 | 6.75 | 7.75 | 9.75 | ||
| s | Nominal | 2.1 | 2.4 | 2.8 | 2.8 | 3.2 | 3.2 | 4 | 4 | 6 | 6 | |
| Max | 2.25 | 2.55 | 2.95 | 2.95 | 3.4 | 3.4 | 4.2 | 4.2 | 6.2 | 6.2 | ||
| Min | 1.95 | 2.25 | 2.65 | 2.65 | 3 | 3 | 3.8 | 3.8 | 5.8 | 5.8 | ||
| h | Min | 3.35 | 3.9 | 4.5 | 4.5 | 5.1 | 5.1 | 6.5 | 6.5 | 9.5 | 10.3 | |
| Max | 3.65 | 4.3 | 5.1 | 5.1 | 5.9 | 5.9 | 7.5 | 7.5 | 10.5 | 11.3 | ||
| Thousand pieces of weight (steel)≈kg | 3.2 | 4.8 | 7 | 7.8 | 12.2 | 13.3 | 21.5 | 23.7 | 42.5 | 68 | ||
Material
| 304 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 | |
| 304 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
| 316 Chemical Composition(%) | ||||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | Cu | MO | N |
| 0.017 | 0.98 | 0.25 | 0.0016 | 0.0414 | 16.23 | 10.08 | 0.32 | 2.06 | 0.037 | |
| 316 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |