| Quantity: | |
|---|---|
GS
Stainless Steel Sleeve Anchor Bolts
Product Name | Stainless Steel Sleeve Anchor Bolts With Hook |
Material | Stainless Steel 304/316/316L A2/A4 |
OEM/Custom | YES |
Feature | 1.Corrosion resistant 2.Excellent life cycle 3.Environmentally friendly 4.High-Performance Fastening |
Standard Available | GB, DIN, ISO, ANSI, ASME, IFI, JIS, BSW, AS, Q, HJ, BS, PEN |
Material Available | Stainless Steel Titanium and Titanium Alloy Aluminum |
Packing | Box+Carton +Pallet or as per client's requirement |
Material
| 304 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 | |
| 304 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
| 316 Chemical Composition(%) | ||||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | Cu | MO | N |
| 0.017 | 0.98 | 0.25 | 0.0016 | 0.0414 | 16.23 | 10.08 | 0.32 | 2.06 | 0.037 | |
| 316 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
Stainless Steel Sleeve Anchor Bolts
Product Name | Stainless Steel Sleeve Anchor Bolts With Hook |
Material | Stainless Steel 304/316/316L A2/A4 |
OEM/Custom | YES |
Feature | 1.Corrosion resistant 2.Excellent life cycle 3.Environmentally friendly 4.High-Performance Fastening |
Standard Available | GB, DIN, ISO, ANSI, ASME, IFI, JIS, BSW, AS, Q, HJ, BS, PEN |
Material Available | Stainless Steel Titanium and Titanium Alloy Aluminum |
Packing | Box+Carton +Pallet or as per client's requirement |
Material
| 304 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 | |
| 304 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
| 316 Chemical Composition(%) | ||||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | Cu | MO | N |
| 0.017 | 0.98 | 0.25 | 0.0016 | 0.0414 | 16.23 | 10.08 | 0.32 | 2.06 | 0.037 | |
| 316 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |