GB /T 22795 (STG)
GS
Satinless Steel Double Casing Expansion Anchor
Goshen's anchor are made of 304/316 stainless steel, which has a bright color, less corrosion and a lot of size.
Material
| 304 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 | |
| 304 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200HB |
| 316 Chemical Composition(%) | ||||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | Cu | MO | N |
| 0.017 | 0.98 | 0.25 | 0.0016 | 0.0414 | 16.23 | 10.08 | 0.32 | 2.06 | 0.037 | |
| 316 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
Satinless Steel Double Casing Expansion Anchor
Goshen's anchor are made of 304/316 stainless steel, which has a bright color, less corrosion and a lot of size.
Material
| 304 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 | |
| 304 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200HB |
| 316 Chemical Composition(%) | ||||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | Cu | MO | N |
| 0.017 | 0.98 | 0.25 | 0.0016 | 0.0414 | 16.23 | 10.08 | 0.32 | 2.06 | 0.037 | |
| 316 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |