| Quantity: | |
|---|---|
ANSI/ASME B 18.2.3.3M
GS
GSHHB001
Stainless Steel Heavy Hex Bolt
stainless steel heavy hex bolt can be used in many different applications, including fastening timbers, steels and other building materials for piers, bridges, highway structures and construction projects. Heavy hexagon bolts with forged heads are also commonly used as head bolts.Because of its stainless steel material and compliance with the advantages of the metric system is widely loved by customers.
Specification
| Screw Thread d | Pitch P | k | s | ||
| max | min | max | min | ||
| M5 | 0.8 | 3.74 | 3.26 | 8 | 7.64 |
| M6 | 1 | 4.42 | 3.76 | 10 | 9.64 |
| M7 | 1 | 5.04 | 4.56 | 11 | 10.57 |
| M8 | 1.25 | 5.54 | 5.06 | 13 | 12.57 |
| M10 | 1.5 | 6.69 | 6.11 | 17 | 16.57 |
| M12 | 1.75 | 7.79 | 7.21 | 19 | 18.48 |
| M14 | 2 | 9.09 | 8.51 | 22 | 21.16 |
| M16 | 2 | 10.29 | 7.91 | 24 | 23.16 |
| M18 | 2.5 | 11.85 | 11.15 | 27 | 26.15 |
| M20 | 2.5 | 12.85 | 12.15 | 30 | 29.16 |
| M22 | 2.5 | 14.35 | 13.65 | 32 | 31 |
| M24 | 3 | 15.35 | 14.65 | 36 | 35 |
| M27 | 3 | 16.65 | 17.35 | 41 | 40 |
| M30 | 3.5 | 19.12 | 18.28 | 46 | 45 |
| M33 | 3.5 | 21.42 | 20.58 | 50 | 49 |
| M36 | 4 | 22.92 | 22.08 | 55 | 53.8 |
Material
| 304 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 | |
| 304 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
| 316 Chemical Composition(%) | ||||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | Cu | MO | N |
| 0.017 | 0.98 | 0.25 | 0.0016 | 0.0414 | 16.23 | 10.08 | 0.32 | 2.06 | 0.037 | |
| 316 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
Stainless Steel Heavy Hex Bolt
stainless steel heavy hex bolt can be used in many different applications, including fastening timbers, steels and other building materials for piers, bridges, highway structures and construction projects. Heavy hexagon bolts with forged heads are also commonly used as head bolts.Because of its stainless steel material and compliance with the advantages of the metric system is widely loved by customers.
Specification
| Screw Thread d | Pitch P | k | s | ||
| max | min | max | min | ||
| M5 | 0.8 | 3.74 | 3.26 | 8 | 7.64 |
| M6 | 1 | 4.42 | 3.76 | 10 | 9.64 |
| M7 | 1 | 5.04 | 4.56 | 11 | 10.57 |
| M8 | 1.25 | 5.54 | 5.06 | 13 | 12.57 |
| M10 | 1.5 | 6.69 | 6.11 | 17 | 16.57 |
| M12 | 1.75 | 7.79 | 7.21 | 19 | 18.48 |
| M14 | 2 | 9.09 | 8.51 | 22 | 21.16 |
| M16 | 2 | 10.29 | 7.91 | 24 | 23.16 |
| M18 | 2.5 | 11.85 | 11.15 | 27 | 26.15 |
| M20 | 2.5 | 12.85 | 12.15 | 30 | 29.16 |
| M22 | 2.5 | 14.35 | 13.65 | 32 | 31 |
| M24 | 3 | 15.35 | 14.65 | 36 | 35 |
| M27 | 3 | 16.65 | 17.35 | 41 | 40 |
| M30 | 3.5 | 19.12 | 18.28 | 46 | 45 |
| M33 | 3.5 | 21.42 | 20.58 | 50 | 49 |
| M36 | 4 | 22.92 | 22.08 | 55 | 53.8 |
Material
| 304 Chemical Composition(%) | ||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 | |
| 304 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |
| 316 Chemical Composition(%) | ||||||||||
| Grade | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | Ni | Cu | MO | N |
| 0.017 | 0.98 | 0.25 | 0.0016 | 0.0414 | 16.23 | 10.08 | 0.32 | 2.06 | 0.037 | |
| 316 Mechanical property | |||
| σb≥ | σ0.2≥ | δ5 (%)≥ | Hardness(HB)(kgf/mm2)] |
| 520(Mpa) | 205(Mpa) | 40% | ≤187 HRB≤90 HV ≤200 |